CNT@CoSx/NiCo-LDH纳米复合材料的制备及其电化学性能研究
编号：42
稿件编号：166 访问权限：仅限参会人
更新：2022-03-03 09:37:58 浏览：293次
口头报告
报告开始：暂无开始时间 （Asia/Shanghai）
报告时间：暂无持续时间
所在会议：[暂无会议] » [暂无会议段]
暂无文件
摘要
TherhombododecahedralCNT@CoS/NiCo-LDHcompositeelectrodematerialwaspreparedbymechanicalstirringandetchingprecipitationmethod.TheelectrochemicaltestresultsshowthattheCNT@CoS/NiCo-LDH-100exhibitshighspecificcapacitanceof2794.6Fg-1at1Ag-1,whichissuperiortoothermaterialswiththeadditionofnickelsource.Whenthecurrentdensityincreasesto5Ag-1,thecapacitanceretentionis60.1%.Inthetwo-electrodesystem,thespecificcapacitanceofCNT@CoS/NiCo-LDH-100is114.1Fg-1(1Ag-1)andexcellentstabilitywith87%after1000cycles.Thedeviceexhibitsarelativelyhighenergydensityof35.64Whkg-1atapowerdensityof750Wkg-1,andevenatthehighpowerdensityof3750Wkg-1,theenergydensityofCNT@CoS/NiCo-LDHmaterialcanstillmaintain26.38Whkg-1.Hence,thesuperiorpseudocapacitiveperformanceofCNT@CoS/NiCo-LDHcanbeascribedtothesynergyamongthreematerialsaswellastheexcellentthree-dimensionalstructureobtainedbychangingamountofnickelsource.
关键字
混合型超级电容器；,复合材料,电化学性能
报告人
发表评论